PETRO-UPE-N-165 Orthophthalic Unsaturated Polyester Resin

This product is used in:

  • Hand layup process.
  • Marine application and flotation of the barge.
  • Composite pipes and Chemical tanks.

Applications

  • Hand layup process.
  • Marine application and flotation of the barge.
  • Composite pipes and Chemical tanks.

Product data

Test method Value Unit Properties
clear Appearance
ASTM D1544 Gardner 2> color
ISO 62 Mpa.s(cp) 400-600 Viscosity brookfield
ASTM D1475 g/cm³ 1/340 Density
ASTM D1980-99 mg KOH/g 15-25 Acid number
ASTM D1259 wt% 63±2 Solid content
ASTM D2471 min 10-25 Gel time
ASTM D2471 min 7-15 Curing time
ASTM D2471 °C 150-185 Peak temperature
ISO 62 wt% 0/0.25 Water absorption

Mechanical Properties

Test method Value Unit Properties
ISO 527-2 MPa 50< Tensile strength
ISO 527-2 % 8.2 Elongation at break
ISO 527-2 MPa 523 Tensile modulus
ISO 178 MPa 110< Flexural strength
ISO178 MPa 2509 Flexural modulus
ASTM D 648 °C >55 Heat distortion temperature
ASTM D2583 >45 Hardness (Barcol)
ASTM D2566 % <1/2 Liner shrinkage

Safety

Material safety datasheets of the product is available on demand.

Storage condition

PETRO-UPE-N-165 Store the product in a cool place at a temperature between 5 to 25 degrees Celsius and avoid keeping material exposed to sunlight. If the mentioned conditions are met, the useful life of the product is 6 months in winter and 3 months in summer from the time of delivery.

Packaging

200 kg (net) in steel drums and bulk road tankers.

Reviews

There are no reviews yet.

Be the first to review “PETRO-UPE-N-165 Orthophthalic Unsaturated Polyester Resin”

Your email address will not be published. Required fields are marked *

Scroll to Top
Scroll to Top